铁艺护栏的生产流程

The production process of iron guardrails

　　铁艺护栏有效、实用的防锈方法是热浸镀锌。即在铁艺护栏在熔化的锌液中在表面生成锌铁合金层及纯锌层，用以隔绝铁艺工件被氧化的机会。防锈期长达20-50年以上，期间无需维修，可靠，是铁艺工件的防锈方法

The most effective and practical rust prevention method for iron guardrails is hot-dip galvanizing. A zinc iron alloy layer and a pure zinc layer are formed on the surface of the iron guardrail in the molten zinc liquid to isolate the opportunity for oxidation of the iron workpiece. The rust prevention period can last for more than 20-50 years, during which no maintenance is required. It is safe and reliable, and is the best rust prevention method for iron workpieces

　　热浸镀锌的工艺流程

The process flow of hot-dip galvanizing

　　1、酸洗前检查处理　检查铁艺工件是否具备本厂镀锌的工艺孔（排气、出入锌夜、吊挂），铁艺工件表面的锈蚀程度，表面覆盖物能否被盐酸除去（如有油漆、油脂等应采用火烧、打磨、碱洗等法除去）。

1. Before pickling, check and treat whether the iron workpiece has the process holes for galvanizing in our factory (exhaust, entry and exit of zinc, hanging), the degree of rust on the surface of the iron workpiece, and whether the surface covering can be removed by hydrochloric acid (if there is paint, grease, etc., it should be removed by methods such as burning, polishing, and alkaline washing).

　　2、脱脂（碱洗）　配有加热设备，铁艺工件表面的油脂、涂料等。

2. Degreasing (alkaline washing) is equipped with heating equipment to eliminate grease, coatings, etc. on the surface of iron workpieces.

　　3、水洗　铁艺工件表面的碱水及附着物。

3. Wash with water to remove alkaline water and attachments from the surface of iron workpieces.

　　4、酸洗　除去铁锈、氧化皮等其它表面覆盖物

4. Pickling to remove rust, oxide skin, and other surface coverings

　　5、酸洗后检查处理：　酸洗效果是否理想，如酸洗不充分，再次酸洗，如果酸洗前处理不彻底，需重新处理后再次酸洗。

5. Post pickling inspection and treatment: Check if the pickling effect is ideal. If the pickling is not sufficient, rinse again. If the pre pickling treatment is not thorough, rinse again after reprocessing.

　　6、水洗　除去铁艺工件表面的酸水及其它附着物

6. Water washing to remove acid water and other attachments on the surface of iron workpieces

　　7、上助镀剂　再次清洗工件表面，保证表面在镀锌之前不在生锈。

7. Clean the surface of the workpiece again with the plating aid to ensure that the surface does not rust before galvanizing.

　　8、烘干　提高铁艺工件温度，避免铁艺表面水分过多，在镀锌时发生爆炸。

8. Drying increases the temperature of iron workpieces to avoid excessive moisture on the surface of the iron, which can cause explosions during galvanizing.

　　9、热浸锌　工件浸泡于440℃-470℃熔融的锌液中，达到一定时间后提出，铁艺工件表面被获得一层锌铁合金层和纯锌层镀层。

9. The hot-dip zinc workpiece is immersed in a molten zinc solution at 440 ℃ -470 ℃, and after a certain period of time, a zinc iron alloy layer and a pure zinc layer coating are obtained on the surface of the ironwork workpiece.

　　10、钝化　提供工件表面抗大气的腐蚀性能，减少或延长白锈出现的时间。

10. Passivation provides the surface of the workpiece with atmospheric corrosion resistance, reducing or prolonging the time for white rust to appear.

　　11、冷却　防止工件激冷回缩，产生集体组织开裂。

11. Cooling prevents the workpiece from being quenched and recoiled, resulting in collective tissue cracking.

　　12、精整　锌瘤及附着在镀层表面的锌灰

12. Fine cleaning of zinc nodules and zinc ash adhering to the surface of the coating

　　13、检验　镀层的检验和测定，工件的外观检查。

13. Inspection and measurement of coating, and visual inspection of workpieces.